A detailed mechanical analysis of the pull-out type in-situ modulus test often used for determination of the primary coating modulus was performed. It was shown that the rigid-rod assumption for the glass fiber is not valid. As a consequence of glass fiber stretch, values obtained for the primary modulus are too low. Correction equations, taking stretch in both the embedded and the non-embedded part of the glass fiber into account, are derived. Using these corrections more accurate values for the primary coating modulus are obtained. Additionally, a very easy to use new mechanical clamping system, not requiring glue to mount the fiber, is introduced. Results for some coated fibers included, illustrate the use of the new clamp and show the importance of the required corrections.
机译：对通常用于确定一次涂层模量的拉出式原位模量测试进行了详细的机械分析。结果表明，玻璃纤维的刚性杆假设是无效的。由于玻璃纤维的拉伸，获得的一次模量值太低。推导了校正方程，其中考虑了在玻璃纤维的嵌入部分和未嵌入部分中的拉伸。使用这些校正，可以获得更精确的底涂层模量值。另外，引入了一种非常易于使用的新型机械夹持系统，不需要胶水来安装光纤。包括一些涂层纤维的结果，说明了新夹具的使用，并表明了进行必要校正的重要性。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号