Sulfide Stress Cracking in Steels - A Review

机译：钢中的硫化物应力开裂-综述

获取原文
获取原文并翻译 | 示例
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Sulfide stress cracking (SSC) has been the subject of investigation since the late 1940's, when a mysterious form of brittle failure began to be observed in steel equipment used to produce oil and gas containing hydrogen sulfide. While the role of hydrogen sulfide in promoting increased levels of hydrogen in steels was recognized early on, researchers disagreed on the mechanism responsible for SSC. Initial theories that SSC was a form of stress corrosion cracking eventually gave way to the current understanding that the phenomenon is caused by hydrogen embrittlement. Research into the effects of hardness, microstructure, chemical composition, and other factors in determining the susceptibility of steels to SSC led to the establishment of industry standards for SSC-resistant materials.
机译：自1940年代末以来，就一直在研究硫化物应力开裂（SSC），当时在用于生产含硫化氢的石油和天然气的钢制设备中开始观察到一种神秘的脆性破坏形式。尽早就认识到硫化氢在促进钢中氢含量增加中的作用，但研究人员不同意造成SSC的机理。最初的理论认为，SSC是应力腐蚀开裂的一种形式，最终被目前的理解认为是由氢脆引起的。对硬度，微观结构，化学成分和其他因素在确定钢对SSC敏感性的影响方面的研究导致建立了耐SSC材料的行业标准。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号