This work explores applications of constraint designed fracture specimens in defect assessments of pressurized pipelines and cylindrical vessels. The primary objective is to gain some understanding of the potential applicability of SE(T) specimens in defect assessments of pressurized pipelines and cylindrical vessels. The present study builds upon the J-Q approach using plane-strain solutions to characterize effects of constraint on cleavage fracture behavior for fracture specimens and cracked pipes. Under increased loading, each cracked configuration follows a characteristic J-Q trajectory which enables comparison of the corresponding crack-tip driving force. A key outcome of this investigation is that toughness data measured using SE(T) specimens appear more applicable for cleavage fracture predictions of pressurized pipelines and cylindrical vessels than standard, deep notch fracture specimens under bend loading. The results encourage further development of constraint-designed SE(T) specimens for fracture assessments of pressurized pipes and cylindrical vessels.

机译：这项工作探讨了约束设计的断裂标本在加压管道和圆柱形容器的缺陷评估中的应用。主要目的是对SE（T）样品在加压管道和圆柱容器的缺陷评估中的潜在适用性有所了解。本研究建立在使用平面应变解决方案的J-Q方法的基础上，以表征约束条件对断裂标本和破裂的管道的劈裂断裂行为的影响。在增加的载荷下，每个裂纹构型都遵循特征性的J-Q轨迹，从而可以比较相应的裂纹尖端驱动力。这项研究的关键成果是，与标准的深切口缺口试样在弯曲载荷下相比，使用SE（T）试样测量的韧性数据似乎更适用于加压管道和圆柱容器的劈裂断裂预测。结果鼓励进一步开发用于压力管道和圆柱形容器断裂评估的约束设计SE（T）标本。

著录项

来源
《ASME(American Society of Mechanical Engineers) Pressure Vessels and Piping Conference vol.3: Design and Analysis; 20050717-21; Denver,CO(US)》|2005年|P.237-246|共10页
会议地点 DenverCO(US)
作者
Sebastian Cravero; Claudio Ruggieri;
展开▼
作者单位

Department of Naval Architecture and Ocean Engineering, University of Sao Paulo Sao Paulo, SP 05508-900, Brazil;

展开▼
会议组织
原文格式 PDF
正文语种 eng
中图分类压力容器;
关键词

相似文献

外文文献
中文文献
专利

1. Correlation of fracture behavior in high pressure pipelines with axial flaws using constraint designed test specimens. Part II: 3-D effects on constraint [J] . L. A. L. Silva, S. Cravero, C. Ruggieri Engineering Fracture Mechanics . 2006,第15期

机译：使用约束设计的试样，对具有轴向缺陷的高压管道的断裂行为进行关联。第二部分：3D对约束的影响
2. Correlation of fracture behavior in high pressure pipelines with axial flaws using constraint designed test specimens-Part I: Plane-strain analyses [J] . Sebastian Cravero, Claudio Ruggieri Engineering Fracture Mechanics . 2005,第9期

机译：使用约束设计的试件对具有轴向缺陷的高压管道的断裂行为进行关联-第一部分：平面应变分析
3. Characterization and correlation of 3-D creep constraint between axially cracked pipelines and test specimens [J] . Tan J. P., Tu S. T., Wang G. Z., Engineering Fracture Mechanics . 2015,第Null期

机译：轴向裂缝管道与试样之间的3D蠕变约束的表征与相关性
4. NUMERICAL CORRELATION OF FRACTURE BEHAVIOR IN AXIALLY CRACKED PIPELINES USING CONSTRAINT DESIGNED FRACTURE SPECIMENS [C] . Sebastian Cravero, Claudio Ruggieri ASME Pressure Vessels and Piping Conference . 2005

机译：使用约束设计裂缝标本轴向裂纹管道裂缝行为的数值相关性
5. Three-dimensional Fracture Mechanics Analyses of Single Edge Cracked Plate Specimens. [D] . Jin, Zhaoyu. 2012

机译：单边裂纹板试样的三维断裂力学分析。
6. Experimental and Numerical Investigation of the Fracture Behavior of Welded Aluminum Cross Joints under Axial Compression [O] . Hannes Panwitt, Horst Heyer, Manuela Sander 2020

机译：轴压下焊接铝交接头断裂行为的实验性和数值研究
7. Erratum to: “Numerical investigation of the transferability of ductile fracture behavior between thin-walled surface-cracked pipe, curved wide plate (CWP) and single edge notched tension (SENT) specimens” [O] . Youn-Young Jang, Ik-Joong Kim, Nam-Su Huh, 2019

机译：错误至：“薄壁表面裂纹管，曲面宽板（CWP）和单边缘缺口张力（送）样本之间的延性断裂行为可转移性的数值研究
8. Fracture Behavior Prediction for Rapidly Loaded Surface Cracked Specimens. [R] . Kirk, M. T., Hackett, E. M. 1988

机译：快速加载表面裂纹试样的断裂行为预测。

NUMERICAL CORRELATION OF FRACTURE BEHAVIOR IN AXIALLY CRACKED PIPELINES USING CONSTRAINT DESIGNED FRACTURE SPECIMENS

摘要

著录项

相似文献

相关主题

期刊订阅