Joint properties of tilted angles of spin for 6061 aluminum alloys in friction stir welded experiments

机译：6061铝合金搅拌摩擦焊接实验中旋转倾角的联合特性。

获取原文
获取原文并翻译 | 示例
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The applicability of friction stir welding to 6061 aluminum alloy with a cylinder-screw-shaped S45C steel spin has been investigated. Three different tilted angles of spin were designed in the friction stir welding experiments. Experimental results have shown that surface defects at spin tilted angle were not observed at the weld zone such as face, toe and root of the weld, and a concentric onion ring pattern with increasing tilted angle of spin appears to be faintly visible. The tensile strength of the butt joints of tilted angles of spin are found to be higher that that of the normal. Also, butt joints through tilted angles of spin are higher than that of substrate matrix, while the tensile strength of the normal was less that that of the substrate matrix. The proposed procedure was applied at butt joints of friction stir welding, and the implementation results demonstrated its feasibility and effectiveness to improve tensile tested experiments for developing robust friction stir welding
机译：研究了搅拌摩擦焊在圆柱螺纹S45C钢旋压6061铝合金上的适用性。在摩擦搅拌焊接实验中设计了三种不同的旋转倾斜角。实验结果表明，在焊接区域（如焊缝的表面，趾部和根部）未观察到自旋倾斜角的表面缺陷，并且随着自旋倾斜角的增加，同心洋葱圈图案似乎微弱可见。发现自旋倾斜角的对接接头的抗拉强度高于法线。而且，通过旋转的倾斜角的对接接头高于基底基质的对接接头，而法线的拉伸强度小于基底基质的抗拉强度。将该方法应用于搅拌摩擦焊的对接接头，实施结果证明了其可行性和有效性，可以改进抗拉试验，以开发可靠的搅拌摩擦焊。