首页> 外文会议>Inorganic thin films and coatings >Preparation of NASICON disk by tape casting and its CO_2 sensing properties
【24h】

Preparation of NASICON disk by tape casting and its CO_2 sensing properties

机译：胶带铸造NASICON圆片的制备及其CO_2传感性能

获取原文
获取原文并翻译 | 示例
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this work, NASICON-type disks with the formula, Na_3Zr_2Si_2PO_(12) were prepared by non-aqueous tape casting method. The effect of the dispersant on the slurry viscosity was investigated, triethanolamine was found to be an effective dispersant for NASICON slurry. The correlation between the overall conductivity and the sintering conditions (temperature and time) for the NASICON disk was also studied. Green tapes were calcined at 900℃, 1000℃, 1100℃ for 6h and 12h, respectively. Results revealed that the overall conductivity increased with the increasing of the sintering temperature and decreased with the increasing of the sintering time. The segregation of resistive monoclinic ZrO_2 phase was examined to have a negative effect on the overall conductivity. The CO_2 sensor using NASICON disk and Li_2CO_3-BaCO_3 complex thick film was fabricated and evaluated, the sensitivity was about 82.9 mV/decade at 450℃.
机译：在这项工作中，通过非水带流延法制备了具有Na_3Zr_2Si_2PO_（12）公式的NASICON型磁盘。研究了分散剂对浆料粘度的影响，发现三乙醇胺是NASICON浆料的有效分散剂。还研究了NASICON盘的总电导率与烧结条件（温度和时间）之间的相关性。生带分别在900℃，1000℃，1100℃下煅烧6h和12h。结果表明，总电导率随烧结温度的升高而增加，随烧结时间的增加而降低。检查了电阻性单斜晶ZrO_2相的偏析对总电导率有负面影响。使用NASICON磁盘和Li_2CO_3-BaCO_3复合厚膜制作了CO_2传感器，并进行了评估，在450℃下灵敏度约为82.9mV /十倍。

著录项

  • 来源
    《Inorganic thin films and coatings》|2012年|134-139|共6页
  • 会议地点 Guilin(CN)
  • 作者

    Jianguo Li; Xishuang Liang; Chengguo Yin; Fengmin Liu; Geyu Lu;

  • 作者单位

    State Key Laboratory on Integrated Optoelectronics Jilin University Region and College of Electronic Science and Engineering, Changchun, PR China;

    State Key Laboratory on Integrated Optoelectronics Jilin University Region and College of Electronic Science and Engineering, Changchun, PR China;

    State Key Laboratory on Integrated Optoelectronics Jilin University Region and College of Electronic Science and Engineering, Changchun, PR China;

    State Key Laboratory on Integrated Optoelectronics Jilin University Region and College of Electronic Science and Engineering, Changchun, PR China;

    State Key Laboratory on Integrated Optoelectronics Jilin University Region and College of Electronic Science and Engineering, Changchun, PR China;

  • 会议组织
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类
  • 关键词

    NASICON; Tape casting; CO_2 sensor;

    机译：NASICON;胶带铸造； CO_2传感器;

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号