The kinetics of isothermal bainite formation at 483 K, 503 K and 533 K in a bearing SAE 52100 steel (1,01% C - 1,36% Cr - 0,32% Mn - 0,25% Si (wt.%)) is investigated theoretically and experimentally. It is found that the bainite formation becomes significantly slower with decreasing temperature. To interpret the results, a physical model with a concept of reconstructive approach proposed in the literature is applied. The model gives a reasonable agreement with experimental results, although a certain deviation exists at the late stage of the transformation. This deviation is attributed to the diffusion coefficient used in the model without considering the effect of alloying elements, mainly chromium.
机译：轴承SAE 52100钢（1,01％C-1,36％Cr-0.32％Mn-0.25％Si（wt。％）在483 K，503 K和533 K时等温贝氏体形成的动力学）进行了理论和实验研究。发现随着温度的降低，贝氏体的形成变得明显变慢。为了解释结果，使用了文献中提出的具有重构方法概念的物理模型。该模型与实验结果给出了合理的一致性，尽管在转换的后期存在一定的偏差。该偏差归因于模型中使用的扩散系数，而不考虑合金元素（主要是铬）的影响。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号