Effect of Cu-Ni Plasma Coating on Fretting Fatigue Characteristics of T1-6AI-4V Under Flat-on-Flat Contact

机译：铜-镍等离子体涂层对平面接触下T1-6AI-4V微动疲劳特性的影响

获取原文
获取原文并翻译 | 示例
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The fretting fatigue tests of Ti-6Al-4V were carried out using Cu-Ni plasma coated and as-received pads (un-coated pads). Fretting fatigue tests of Ti-6Al-4V, where Cu-Ni plasma coated and as-received pads were used, repeatedly were also carried out. The characterization of pads before and after testing were carried out in order to investigate the mechanism of fretting fatigue of Ti-6Al-4V in contact with the Cu-Ni plasma coated pad used. Cu-Ni plasma coating on the pads prolonged the fretting fatigue life of Ti-6Al-4V. The fretting fatigue life of Ti-6Al-4V decreased with repeated use of test when the Cu-Ni plasma coated pads. On the other hand, the opposite trend was observed when the as-received pads were repeatedly used. The surfaces of Cu-Ni plasma coated pads were smoother after testing than before testing due to the plastic deformation. On the other hand, the surface of as-received pads were rougher after testing than before testing.
机译：Ti-6Al-4V的微动疲劳试验是使用经Cu-Ni等离子涂覆和接收的垫板（未涂覆的垫板）进行的。还重复进行了Ti-6Al-4V的微动疲劳试验，在该试验中使用了Cu-Ni等离子涂层和已接收的焊盘。为了研究Ti-6Al-4V与所用的Cu-Ni等离子镀膜垫接触后的微动疲劳机理，在测试前后对它们进行了表征。垫上的Cu-Ni等离子涂层延长了Ti-6Al-4V的微动疲劳寿命。当铜-镍等离子涂层垫反复使用时，Ti-6Al-4V的微动疲劳寿命降低。另一方面，当重复使用所接收的垫时，观察到相反的趋势。测试后，由于塑性变形，与测试前相比，Cu-Ni等离子涂层焊盘的表面更光滑。另一方面，测试后的接收垫的表面比测试前更粗糙。