The effects of didymium(Nd: Pr = 3: l)on the microstructure and mechanical properties of Mg-10% Al alloy were studied with the additions of 0～3%Di. The small block-like Al_2(Nd,Pr) phase appears in l%Di alloy, the blocklike Al_2(Nd,Pr) and needle-like Al_(11)(Nd,Pr)_3 phases appear synchronously in 2%Di and 3%Di alloys, while the network of (Mg_(17)Al_(12)) β phase is broken up. The tensile properties can be improved with the addition of didymium. When the addition of didymium in Mg-10%Al alloy reaches 2% , the alloy exhibits the best combination of strength and ductility , but the strength and ductility drop at the addition of 3 % Di due to the obvious increase of the size and quantity of the needle-like Al_(11)(Nd,Pr)_3 phase.
机译：研究了掺钕（Nd：Pr ＝ 3：1）对Mg-10％铝合金的组织和力学性能的影响，添加了0〜3％Di。在1％Di合金中出现小块状Al_2（Nd，Pr）相，在2％Di和3中同步出现块状Al_2（Nd，Pr）和针状Al_（11）（Nd，Pr）_3相。 ％Di合金，而（Mg_（17）Al_（12））β相的网络破裂。可以通过添加did来改善拉伸性能。当Mg-10％Al合金中钕的含量达到2％时，合金表现出强度和延性的最佳组合，但Di的含量和强度的下降则是由于尺寸和数量的明显增加而降低的。针状Al_（11）（Nd，Pr）_3相的相变。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号