首页> 外文会议>International Symposium on Nitrides; 20060403-05; Eskisehir(TK) >Pressureless Sintering of Hexagonal Boron Nitride Powders
【24h】

Pressureless Sintering of Hexagonal Boron Nitride Powders

机译：六方氮化硼粉末的无压烧结

获取原文
获取原文并翻译 | 示例
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Pressureless sintering of hexagonal boron nitride (BN) with and without additives was performed using a powder which was previously nitrided at 900℃ and then heat treated at 1400℃. Sintering additives were B_2O_3 (2, 4, 6 wt %) and Y_2O_3 (2, 4, 6 wt %) and sintering temperatures was 1900℃. Sintered samples were characterized by XRD, SEM, micro hardness, density and mercury porosimeter measurements. Maximum density values of samples were 1.56 g/cm~3 without additives and 1.63 g/cm~3 with additives. Hardness values of samples were found to improve with the presence of additives.
机译：使用预先在900℃进行氮化，然后在1400℃进行了热处理的粉末，对有无添加剂的六方氮化硼（BN）进行无压烧结。烧结添加剂为B_2O_3（2、4、6 wt％）和Y_2O_3（2、4、6 wt％），烧结温度为1900℃。通过XRD，SEM，显微硬度，密度和水银孔隙率仪对烧结样品进行表征。不含添加剂的样品的最大密度值为1.56 g / cm〜3，含添加剂的样品的最大密度值为1.63 g / cm〜3。发现样品的硬度值随着添加剂的存在而提高。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号