A new insight into the mechanistic study on synthesis of Silica Nanospheres

机译：二氧化硅纳米球合成机理研究的新见解

获取原文
获取原文并翻译 | 示例
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The physicochemical characteristics (SEM, N_2 adsorption, FT-IR, MASNMR) of samples from kinetics (10 min, 20 min, 30 min, 1 h and 3h) of hydrolysis of tetraethyl orthosilicate (TEOS) gives new insight into the synthesis of nanosphere. The particle sizes are increased with time, however, the surface areas decreased. FT-IR investigation reveals the presence of high intensed silanol groups of 960 cm~(-1) at 10 min, which reduced on progress of the reaction time. This suggests the partial hydrolysis and condensation of alkoxy groups in TEOS. ~(29)Si MASNMR analysis shows the presence three different silica species(Q_4, Q_3 and Q_2) in 10 and 20 min samples. The intensity of Q_2 species decreases with time and other species concentration were increased.
机译：原硅酸四乙酯（TEOS）水解动力学（10分钟，20分钟，30分钟，1小时和3小时）的样品的理化特性（SEM，N_2吸附，FT-IR，MASNMR）为纳米球的合成提供了新见识。粒度随时间增加，但是表面积减小。 FT-IR研究表明，在10分钟时存在960 cm〜（-1）的高强度硅烷醇基，随着反应时间的延长，硅烷基的数量减少。这表明TEOS中烷氧基的部分水解和缩合。 〜（29）Si MASNMR分析显示在10和20分钟的样品中存在三种不同的二氧化硅种类（Q_4，Q_3和Q_2）。 Q_2物种的强度随时间降低，其他物种的浓度增加。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号