An Accelerated Electrolytic Corrosion Test For the Cu-Ni-Cr Plating System on the Intricate Shape Details

机译：复杂形状的Cu-Ni-Cr电镀系统的加速电解腐蚀试验

获取原文

页面导航

摘要
著录项
相似文献
相关主题

摘要

A method of corrosion resistance prediction of Cu-Ni-Cr-coatings by the results of accelerated corrosion tests and by atmospheric corrosion tests in different conditions has been proposed. Accelerated tests were performed by cyclic potentiostatic anodic dissolution. The grouth of the corrosion spots in the coatings was estimated by the coulopotentiograms. A special electrochemical cell was constracted for test intricate shape details. The digital results of control corrosion resistance Cu-Ni-Cr coatings can be used for statistical operating technological processes.

机译：提出了一种通过加速腐蚀试验结果和不同条件下的大气腐蚀试验结果预测Cu-Ni-Cr涂层抗腐蚀性能的方法。通过循环恒电位阳极溶解进行加速测试。涂层中腐蚀点的增长通过电位电位图估算。为了测试复杂的形状细节，专门设计了一个电化学电池。控制耐腐蚀Cu-Ni-Cr涂层的数字结果可用于统计操作技术过程。

著录项

来源
《SUR/FIN-1996 international technical conference》|1996年|p.891-894|共4页
会议地点
作者
Rustem A. Kaidrikov; Boris L. Juravlev;
展开▼
作者单位

展开▼
会议组织
原文格式 PDF
正文语种
中图分类金属学与金属工艺;
关键词

相似文献

外文文献
中文文献
专利

1. Corrosion mechanisms of Zn(Mg, Al) coated steel in accelerated tests and natural exposure: 1. The role of electrolyte composition in the nature of corrosion products and relative corrosion rate [J] . M. Salgueiro Azevedo, C. Allely, K. Ogle, Corrosion science . 2015,第jana期

机译：加速试验和自然暴露中的Zn（Mg，Al）涂层钢的腐蚀机理：1.电解质成分在腐蚀产物的性质和相对腐蚀速率中的作用
2. Corrosion analysis of decorative microporous chromium plating systems in concentrated aqueous electrolytes [J] . Langer C., Wendland W., Honold K., Engineering failure analysis . 2018,第期

机译：浓缩水性电解质中装饰微孔铬镀系统的腐蚀分析
3. Corrosion analysis of decorative microporous chromium plating systems in concentrated aqueous electrolytes [J] . Langer C., Wendland W., Honold K., Engineering failure analysis . 2018,第期

机译：浓缩水性电解质中装饰微孔铬镀系统的腐蚀分析
4. An Accelerated Electrolytic Corrosion Test For the Cu-Ni-Cr Plating System on the Intricate Shape Details [C] . Rustem A. Kaidrikov, Boris L. Juravlev SUR/FIN international technical conference . 1996

机译：Cu-Ni-Cr电镀系统对复杂形状细节的加速电解腐蚀试验
5. Evaluating the corrosion protection of post-tensioning grouts: Standardization of an accelerated corrosion test. [D] . Pacheco, Alexandre R. 2003

机译：评估后张水泥浆的腐蚀防护：加速腐蚀试验的标准化。
6. Influence of Pore Networking and Electric Current Density on the Crack Pattern in Reinforced Concrete Test Due to Pressure Rust Layer at Early Ages of an Accelerated Corrosion Test [O] . Ángela M. Bazán, Encarnación Reyes, Jaime C. Gálvez 2019

机译：早期腐蚀试验中孔网和电流密度对钢筋混凝土试验中压力锈层造成的裂缝模式的影响
7. Problem of Conventional Accelerated Corrosion Tests, and Development of New Accelerated Corrosion Test-Development of New Accelerated Corrosion Test simulating Electrical Appliances Environment (2)- [O] . Hiroshi Kajiyama, Sakae Fujita, Kazumi Fujii, 2006

机译：常规加速腐蚀试验的问题，以及新型加速腐蚀试验的开发新加速腐蚀试验模拟电器环境（2） -

An Accelerated Electrolytic Corrosion Test For the Cu-Ni-Cr Plating System on the Intricate Shape Details

摘要

著录项

相似文献

相关主题

期刊订阅