首页> 外文会议>IUMRS International Conference in Asia;IUMRS-ICA 2010 >Effect on the characteristic and properties of carbon coated LiFePCVC composite
【24h】

Effect on the characteristic and properties of carbon coated LiFePCVC composite

机译：碳包覆LiFePCVC复合材料的特性和性能的影响

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

LiFePCVC composite with different types of organic carbon sources has been synthesized by carbon thermal reduction technique. The physical characteristics and electrochemical properties of LiFePO_4/C composite have been studied compared with commercial products. It is shown that good carbon-coated LiFePCVC composite can be obtained with 13wt.% glucose as carbon source, which has effected on the good processing performance due to its suitable specific surface area of 26.3m~2/g and high tap density of 1.3g/cm~3. Furthermore, it has contributed to the high-rate electrochemical property with discharge capacity of 128mAh/g at 1C (1C=17O mAh/g).
机译：通过碳热还原技术合成了具有不同类型有机碳源的LiFePCVC复合材料。与市售产品相比，研究了LiFePO_4 / C复合材料的物理特性和电化学性能。结果表明，以13wt。％的葡萄糖为碳源可以得到良好的碳包覆LiFePCVC复合材料，其合适的比表面积为26.3m〜2 / g，高振实密度为1.3，对良好的加工性能产生了影响。克/厘米〜3。此外，它还有助于实现高速率的电化学性能，在1C（1C = 17O mAh / g）时的放电容量为128mAh / g。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号