摘要

The influence of one- and two- stage solution heat treatment on the microstructure and mechanical properties of aluminum alloy 7055 was investigated. The results showed that in the case of one-stage solution heat treatment in the range of 450°C to 470°C, the strength increased while the ductility decreased with temperature. Further increasing temperature led to more dissolution of soluble constituents but a large amount of recrystallization, therefore, the strength decreased while ductility increased. The two-stage solution heat treatment, which included first stage of low-temperature-long-duration and second stage of high-temperature-short-duration heating was suggested for improvement of mechanical properties.
机译：研究了一种和两级溶液热处理对铝合金7055微观结构和力学性能的影响。结果表明，在一级溶液热处理的情况下，在450℃至470℃的范围内，强度随温度降低而增加。进一步提高温度导致可溶性成分的更多溶解，但大量的重结晶，因此，在延展性增加时，强度降低。包括包括高温长持续时间和高温短持续时间加热第二阶段的第一阶段的两级溶液热处理以改善机械性能。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号