Prediction of Hardness of Aluminum Alloy 7055 by Quench Factor Analysis

机译：淬火因子分析预测7055铝合金的硬度

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The Vickers hardness time-temperature-properties (TTP) curve of aluminum alloy 7055 was evaluated by interrupted quench technique. The critical temperature range of TTP curve was determined from 210°C to 420°C with the nose temperature of 355°C. The hardness decreased rapidly with isothermal duration in the critical temperature range. The hardness of aluminum alloy 7055 was predicted by quench factor analysis using the TTP curve and cooling curves. The predicted hardness agreed reasonably well with the measured results. The influence of time step and summation temperature range on the predicted results was studied. The cooling rate through the critical temperature range had dominant influence on the final hardness of the alloy.
机译：通过中断淬火技术评估铝合金7055的维氏硬度时间 - 温度 - 性能（TTP）曲线。 TTP曲线的临界温度范围由210℃至420℃测定，鼻温为355℃。硬度随着临界温度范围内的等温持续时间迅速降低。通过使用TTP曲线和冷却曲线通过淬火因子分析预测铝合金7055的硬度。预测的硬度与测量结果相当好。研究了时间步长和求和温度范围对预测结果的影响。通过临界温度范围的冷却速率对合金的最终硬度有显性影响。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号