A sixteen run designed experiment was performed on biaxially oriented PET film with line speed and corona treater power setting as variables. The (corona treater gap was held constant.) on biaxially oriented PET film. Using Atomic Force Microscopy (AFM), surface topography and compositional variations were measured on each sample of treated film. Surface roughness values, Ra, were determined from the AFM images. The surface energy of each sample was obtained from contact angle data immediately after production. Each sample was also aged at 50 deg C for one week and then imaged with AFM again to determine any changes in roughness or composition. The film was washed with deionized water to remove any water soluble low molecular weight material formed in the corona treatment. The material was analyzed with mass spectroscopy and nuclear resonance spectroscopy in an effort to identify the material(s). Comparisons will be made between these results and our prior results of corona treatment of uniaxially oriented PET film.
机译：在双轴导向的PET膜上进行了十六次进行设计的实验，用线速度和电晕分流器电源设置为变量。在双轴导向的PET膜上（电晕操纵间隙保持恒定）。使用原子力显微镜（AFM），在每个处理膜样品上测量表面形貌和组成变化。从AFM图像确定表面粗糙度Ra Ra。每个样品的表面能在生产后立即获得从接触角数据获得。每个样品在50℃下也为50℃，然后再次与AFM成像以确定粗糙度或组成的任何变化。将薄膜用去离子水洗涤，除去在电晕处理中形成的任何水溶性低分子量材料。用质谱和核共振光谱分析该材料以占据鉴定材料。将在这些结果和我们的高度导向PET膜的电晕处理结果之间进行比较。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号