首页> 外文会议>Annual Meeting Exhibition of The Minerals, Metals Materials Society >Carbonation Behavior of Calcium Aluminate Cements with Additions of Silica
【24h】

Carbonation Behavior of Calcium Aluminate Cements with Additions of Silica

机译：添加二氧化硅的铝酸钙水泥的碳酸化行为

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this research different formulations of calcium aluminate cements (CAC) pastes with 51 and 71 wt% (wt%-percentage by weight) Al_2O_3 were made at 0.4 water to cement ratio (W/C) with additions of 0 and 20 wt% silica. Both the raw cement powders and their corresponding samples after hydration were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), density and compression tests. Samples were exposed to 20 °C in a furnace open to air, for 3, 4 and 7 days with a concentration of CO_2 of 4% and relative humidity of 70%.
机译：在本研究中，在0.4水至水泥比（W / C）下，在0.4水中加入0和20wt％二氧化硅，将铝酸钙水泥（CAC）浆料（CAC）浆料的不同配方用51和71重量％（重量％）（wt％-31重量％），加入水泥比（w / c）。 。通过扫描电子显微镜（SEM），X射线衍射（XRD），密度和压缩试验，将原料水泥粉末及其相应的样品进行了表征。将样品暴露于20℃，在向空气开放的炉中，浓度为3,4和7天，浓度为4％，相对湿度为70％。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号