首页> 外文会议>International Conference on Biological Engineering and Pharmacy >Porous In_2O_3 Nanorods: Synthesis and Enhanced NO_x Gas-Sensing Properties at Room Temperature
【24h】

Porous In_2O_3 Nanorods: Synthesis and Enhanced NO_x Gas-Sensing Properties at Room Temperature

机译：多孔in_2O_3纳米棒：在室温下合成和增强的NO_x气体传感性能

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A novel room temperature gas sensor based on porous In_2O_3 nanorods was successfully synthesized via a facile reflux method. The In_2O_3 demonstrates a rod-like shape with a diameter of 10 - 20 nm and a length about 70 - 100 nm, which displays good and uniform size. Studies have shown that the porous In_2O_3 nanorods have the n-type semiconductor characteristic. We demonstrate that it can detect NO_x gas with a sensitivity of 17, fast response of 17.3 s to 97.0 ppm NO_x and a low detection limit of 0.485 ppm at room temperature.
机译：基于多孔IN_2O_3纳米棒的新型室温气体传感器通过容易的回流方法成功地合成。 IN_2O_3演示了直径为10-20nm的杆状形状，长度为约70-100nm，其显示出良好且均匀的尺寸。 研究表明，多孔IN_2O_3纳米棒具有n型半导体特性。 我们证明它可以检测敏感性为17的NO_X气体，快速响应为17.3秒至97.0ppm NO_X，在室温下的低检测限为0.485ppm。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号