THE EFFECT OF FIBER LENGTH AND COARSENESS ON THE TEARING STRENGTH

机译：纤维长度和粗度对撕裂强度的影响

获取原文

获取原文并翻译 | 示例

页面导航

摘要
著录项
相似文献
相关主题

摘要

The effects of fiber length and coarseness of the non-wood fibers on the tearing strength were studied in this paper. SPSS (Statistical Product and Service Solutions) software was used to analysis all the data. In this investigation, the weight-average fiber length could be taken as a parameter of effect of fiber length on tearing strength. The results showed the dependence of tearing strength on fiber length was very strong in a weakly bonded sheet. While for a well-bonded sheet, the dependence of tearing strength on fiber length decreased with the increase of fiber bonding strength. The tearing strength increased with the improvement of the fiber coarseness in a weakly bonded sheet.

机译：研究了纤维长度和非木质纤维的粗度对撕裂强度的影响。 SPSS（统计产品和服务解决方案）软件用于分析所有数据。在该研究中，可以将重均纤维长度作为纤维长度对撕裂强度的影响的参数。结果表明，在弱粘合片中，撕裂强度对纤维长度的依赖性非常强。而对于粘合良好的片材，撕裂强度对纤维长度的依赖性随纤维粘合强度的增加而降低。撕裂强度随着弱粘合片中纤维粗度的提高而增加。

著录项

来源
《New Technologies in Non-wood Fiber Pulping and Papermaking》|2006年|41-44|共4页
会议地点 Guangzhou(CN)
作者
Liu Hongbin; Yang Shuhui; Dong Rongye;
展开▼
作者单位

Tianjin Key Laboratory of Pulp and Paper, Tianjin University of Science and Technology, Tianjin 300222, China;

展开▼
会议组织
原文格式 PDF
正文语种 eng
中图分类造纸工业;
关键词
fiber length; coarseness; nonwood fibers; tearing strength;

机译：纤维长度粗度非木纤维；撕裂强度;

相似文献

外文文献
中文文献
专利

1. Wavelength-Tunable Dispersion Compensating Photonic Crystal Fibers Suitable for Conventional/Coarse Wavelength Division Multiplexing Systems [J] . Hsu Jui-Ming, Yao Che-Wei, Chen Jian-Zhi Lightwave Technology, Journal of . 2015,第11期

机译：适用于常规/粗波分复用系统的波长可调色散补偿光子晶体光纤
2. Effects of Single and Hybrid Steel Fiber Lengths and Fiber Contents on the Mechanical Properties of High-Strength Fiber-Reinforced Concrete [J] . Kyoung-Chul Kim, In-Hwan Yang, Changbin Joh Advances in civil engineering . 2018,第3期

机译：单根和混合钢纤维长度和纤维含量对高强度纤维增强混凝土力学性能的影响
3. Effects of Single and Hybrid Steel Fiber Lengths and Fiber Contents on the Mechanical Properties of High-Strength Fiber-Reinforced Concrete [J] . Kim Kyoung-Chul, Yang In-Hwan, Joh Changbin Advances in civil engineering . 2018,第PTa2期

机译：单根和混合钢纤维长度和纤维含量对高强度纤维增强混凝土力学性能的影响
4. THE EFFECT OF FIBER LENGTH AND COARSENESS ON THE TEARING STRENGTH [C] . Liu Hongbin, Yang Shuhui, Dong Rongye, International Non-wood Fiber Pulping and Papermaking Conference . 2006

机译：纤维长度和粗糙度对撕裂强度的影响
5. A STUDY OF THE EFFECT OF FIBER LENGTH DISTRIBUTION ON THE TEAR STRENGTH OF A SYNTHETIC FIBER SHEET. [D] . FUNDERBURK, KIT. 1968

机译：纤维长度分布对合成纤维板抗撕强度的影响研究。
6. Analysis of Bond Strength by Pull Out Test on Fiber Glass Posts Cemented in Different Lengths [O] . Mariana Benedetti Ferreira Webber, Silvia Masae de Araújo Michida, Fabiano Carlos Marson, 2015

机译：通过拉拔试验分析不同长度的胶合玻璃纤维桩的粘结强度
7. Mechanical properties of various concrete after high temperature exposure Mechanical property of various types of concrete after high temperature exposure is investigated. Considering compressive strength requirement for a vertical element in high rise building, concrete specimens with various design strengths of 35, 80, 100, and 150 MPa were tested. Particularly, the influence of incorporated steel fiber on fire resistance is of interest in this study. Experimental results show that the fire resistance depends on the design strength and steel fiber content. Normal strength concrete (NSC) of a design strength of 35 MPa or high performance concrete (HPC) of 80-100 MPa does not spall when exposed to 100-400 °C of temperature. However, an explosive spalling occurs at 300 °C when the HPCs contain 1 vol. of steel fiber. Ultra-high performance concrete (UHPC) of a design strength of 150 MPa and 1.5 vol. of steel fiber also shows dramatic spalling at 300 °C. The experimental results found in this study can contribute to a better understanding of the behaviors of HPC and UHPC under fire and the role of steel fiber on the fire resistance. [O] . 2017

机译：研究了高温暴露后各种混凝土高温曝光机械性能各种混凝土的机械性能。考虑到高层建筑中垂直元件的抗压强度要求，测试了35,80,100和150MPa各种设计强度的混凝土试样。特别是，在这项研究中，掺入钢纤维对耐火性的影响。实验结果表明，耐火性取决于设计强度和钢纤维含量。在暴露于100-400°C的温度时，80-100MPa的设计强度为35MPa或高性能混凝土（HPC）的正常强度混凝土（NSC）不会击落。然而，当HPC含有1体积的钢纤维的百分比时，爆炸性剥落发生在300℃。超高性能混凝土（UHPC）的设计强度为150 MPa和1.5 Vol。钢纤维的百分比也显示出300℃的剧烈剥落。本研究中发现的实验结果可以有助于更好地了解在火灾中的HPC和UHPC的行为以及钢纤维对耐火性的作用。
8. Multi-mode fiber coarse WDM grating router using broadband add/drop filters for211 wavelength re-use [R] . Patel, R. R., Bond, S. W., Larson, M. C., 1999

机译：多模光纤粗WDm光栅路由器采用宽带分插滤波器，可重复使用211波长

THE EFFECT OF FIBER LENGTH AND COARSENESS ON THE TEARING STRENGTH

摘要

著录项

相似文献

相关主题

期刊订阅