摘要

Most silicate coatings for concrete protection are currently based on potassium water glass. Water glass matrix itself is, however, insufficient for coatings and is modified by polymer substances for the coating purpose. Combinations of water glass basic matrix (Sodium, Potassium, Lithium, Sodium - Lithium and Potassium - Lithium) with the appropriate polymer modifiers is content of the presented research. This paper contains the basic part of the research - the molar ratio influence to water glass coatings basic properties (adhesion, diffusion properties, surface quality, applicability). Polymer dispersions modification effect to developed silicate coating binder is also part of paper.
机译：目前，大多数用于混凝土保护的硅酸盐涂料都基于钾水玻璃。然而，水玻璃基质本身不足以用于涂料，并且为了涂覆目的而被聚合物质改性。水玻璃基本基质（钠，钾，锂，钠-锂和钾-锂）与合适的聚合物改性剂的结合是本研究的内容。本文包含了研究的基础部分-摩尔比对水玻璃涂料的基本性能（附着力，扩散性能，表面质量，适用性）的影响。聚合物分散体对已开发的硅酸盐涂料粘合剂的改性效果也是纸的一部分。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号