首页> 外文会议>Symposium on Magnetic Ultrathin Films,Multilayers and Surface --1997 March 31-April 4,1997, San Francisco, California, U.S.A >Bilinear and biquadratic exchange coupling in Fe(110)/Cr/Fe trilayers
【24h】

Bilinear and biquadratic exchange coupling in Fe(110)/Cr/Fe trilayers

机译：Fe（110）/ Cr / Fe三层中的双线性和双二次交换耦合

获取原文
获取原文并翻译 | 示例
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The indirect exchange coupling in W(110)/Fe/Cr/Fe/Cr trilayers was determined by analysis of magnetization curves measured by Kerr magnetometry. We adjusted the uniaxial in-plane anisotropies in the two Fe layers in such a way that the easy axes were orthogonal, [001] in the 1 st, [110] in the 2nd layer, This allows an independent determination of both bilinear (J_1) and biquadratic (J_2) coupling constants. We determined J_1 and J_2 as a function of Cr interlayer thickness (t_Cr=0-4 nm), preparation temperature of the interlayer T_p,Cr =100-500K, and as a function of temperature (T=100-300 K). Results for the exchange coupling are correlated to the particular lateral thickness fluctuaftion of the Cr spacer.
机译：W（110）/ Fe / Cr / Fe / Cr三层中的间接交换耦合是通过分析由Kerr磁力法测得的磁化曲线确定的。我们调整了两个Fe层中的单轴面内各向异性，使得易轴正交，第一层为[001]，第二层为[110]，这样就可以独立确定两个双线性（J_1 ）和双二次（J_2）耦合常数。我们确定J_1和J_2是Cr中间层厚度（t_Cr = 0-4 nm），中间层的制备温度T_p，Cr = 100-500K和温度（T = 100-300 K）的函数。交换耦合的结果与Cr垫片的特定横向厚度波动相关。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号