H Diffusion in the H-Storage TiVMnCr Alloys as Deduced from Absorption and Mechanical Spectroscopy Experiments

机译：从吸收和机械光谱实验推导的储氢TiVMnCr合金中的H扩散

获取原文
获取原文并翻译 | 示例
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The low H content portion of the PCT absorption curves of the 40Ti-xV-(50-x)Mn-10Cr alloys exhibits a plateau, whose pressure has been determined together with the solubility limit of H in the α-phase (solid solution). The chemical (D_c) and Einstein (D_e) diffusion coefficients of H have been deduced from H absorption kinetics (273 K-1100 K) and from mechanical spectroscopy (150 K-200 K), which has revealed a Snoek-type of anelastic relaxation. The combined Arrhenius plot of D_e and D_c gives the following parameters for H diffusion: W=0.318±0.005 eV, D_0=(4±1)x10~(-7) m~2/s (36 V alloy) and W=0.352±0.005 eV, D_0=(5+1)10~(-7) m~2/s (32 V alloy).
机译：40Ti-xV-（50-x）Mn-10Cr合金的PCT吸收曲线的低H含量部分呈现平稳状态，其压强已确定，并且H在α相（固溶体）中的溶解度极限也已确定。 H的化学（D_c）和Einstein（D_e）扩散系数已从H吸收动力学（273 K-1100 K）和机械光谱学（150 K-200 K）推导得出，这揭示了Snoek型非弹性弛豫。 D_e和D_c的组合Arrhenius图给出了H扩散的以下参数：W = 0.318±0.005eV，D_0 =（4±1）x10〜（-7）m〜2 / s（36 V合金），W = 0.352 ±0.005 eV，D_0 =（5 + 1）10〜（-7）m〜2 / s（32 V合金）。