This thesis presents a new strategy to fabricate nanostructured indium phosphide and cadmium sulfide photovoltaics. The cells are formed by chemical bath deposition (electroless deposition) of cadmium sulfide onto indium phosphide nanopillar arrays grown by selective-area metalorganic chemical vapor deposition. Characterizations through electrical and optical measurements show that the devices consisting of p-InP core and CdS shell have a conversion efficiency, open circuit voltage, short circuit current density and fill factor of 4.8%, 0.53 V, 15.8 mA/cm² and 0.57 respectively. A solution-based junction formation on nanopillars is developed and investigated in search of a quick and low-cost method to harvest solar energy.
机译：本文提出了一种制备纳米结构的磷化铟和硫化镉光伏电池的新策略。这些单元是通过将硫化镉化学浴沉积（化学沉积）到通过选择性区域金属有机化学气相沉积法生长的磷化铟纳米柱阵列上而形成的。通过电学和光学测量的特性表明，由p-InP内核和CdS外壳组成的器件的转换效率，开路电压，短路电流密度和填充系数分别为4.8％，0.53 V，15.8 mA /cm²和0.57。在纳米柱上开发了基于溶液的结，并对其进行了研究，以寻求一种快速，低成本的太阳能收集方法。

著录项

  • 作者

    Tu, Bor-An Clayton.;

  • 作者单位

    University of California, Los Angeles.;

  • 授予单位 University of California, Los Angeles.;
  • 学科 Engineering Electronics and Electrical.
  • 学位 M.S.
  • 年度 2013
  • 页码 41 p.
  • 总页数 41
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类
  • 关键词

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号