首页> 外文学位 >Ferroelectricity and piezoelectricity in nylon 11 films with different draw ratios.
【24h】

Ferroelectricity and piezoelectricity in nylon 11 films with different draw ratios.

机译：不同拉伸比的尼龙11薄膜的铁电性和压电性。

获取原文
获取原文并翻译 | 示例
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

ylon 11 was melted at 210;The melt-quenched undrawn and uniaxially drawn nylon 11 films with draw ratios from 1.5:1 to 3.5:1 all exhibited ferroelectric response. The remanant polarization ;Upon uniaxially drawing the films to a draw ratio 3.5:1 from the undrawn, the glass transition temperature, ;Upon absorbing moisture from the environment, both the glass transition temperature and the piezoelectric transition temperature decreased from ;The electromechanical coupling coefficient,
机译：尼龙11在210熔化；拉伸比为1.5：1至3.5：1的熔融淬火未拉伸和单轴拉伸尼龙11薄膜均表现出铁电响应。剩余极化;在未拉伸时单轴拉伸薄膜至拉伸比3.5：1;玻璃化转变温度;;从环境中吸收水分后，玻璃化转变温度和压电转变温度均从降低;机电耦合系数，

著录项

  • 作者

    Wu, Shiann-Long.;

  • 作者单位

    Rutgers The State University of New Jersey - New Brunswick.;

  • 授予单位 Rutgers The State University of New Jersey - New Brunswick.;
  • 学科 Engineering Materials Science.
  • 学位 Ph.D.
  • 年度 1997
  • 页码 189 p.
  • 总页数 189
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类
  • 关键词

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号