通过在经处理的不锈钢网(SSM)上逐层电纺制备了简易有效的聚酰胺66/聚丙烯腈/聚醚砜(PA-66/PAN/PES)复合纤维过滤材料.材料中间层采用以N,N-二甲基甲酰胺(DMF)为溶剂的PAN/PES共混聚合物电纺而成.扫描电子显微镜表征和比表面积测试结果表明, 在相同纺丝条件下PES量的增加有利于减小纤维直径, 增大膜的孔隙率.同时, 通过拉伸实验测量了未带有SSM的膜的机械性能(5.857 MPa).利用PES的良好疏水性, 过滤膜表面具有相对良好的疏水效果, 接触角约为130.58°.在样品厚度尽可能相等的情况下, 通过对实际空气环境中0.3~5 μm的颗粒进行截流测试发现, PAN/PES-3的过滤效率达到且大于99%.通过机械振动和空气反吹考察了过滤膜的再生性能.此外, 还通过使用喷雾喷涂SSM研究了防分层过滤介质的基质.%A simple and effective composite fiber filter material was prepared which was composed of polyamide-66/polyacrylonitrile/polyethersulfone(PA-66/PAN/PES) fibers with layer by layer on treated stainless steal mesh(SSM).The intermediate layer of the material was dissolved in an N,N-dimethylformaide(DMF) solvent by PAN/PES.With the increase of the amount of PES under the same spinning condition, it is advantageous for the fiber dia-meter to become small and to increase the porosity of the film by the SEM and BET test.Synchronously, the mechanical properties of the films without SSM were measured(5.857 MPa) by tensile test.The surface of the filter membrane has a relatively good hydrophobic effect with contact angle(CA) of 130.58° by making use of the hydrophobicity of PES.In the case of the thickness of the sample as equal as possible, the filtration efficiency of PAN/PES-3 for the particles sized of 0.3_5 μm reached more than 99% by measuring in the actual air environment.The filtered regenerated film was observed by mechanical vibration and air backflush.In addition, we also have explored a substrate for filtered medium by using SSM which was sprayed with water spray to anti-layered.
展开▼