首页> 中文期刊> 《中国铸造：英文版》 >Microstructure and properties of TP2 copper tube with La microalloying by horizontal continuous casting

Microstructure and properties of TP2 copper tube with La microalloying by horizontal continuous casting

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The TP2 copper tube was prepared with La microalloying by horizontal continuous casting(HCC). The absorptivity of La and its effects on microstructure, tensile and corrosion properties of HCC TP2 copper tube were studied by means of the inductively coupled plasma optical emission spectrometer(ICP-OES), optical microscope(OM), scanning electron microscope(SEM) and potentiodynamic polarization measurements. The results show that the absorptivity of La in the HCC TP2 copper tube is about 15% under antivacuum conditions due to the good chemical activities of La. The impurity elements in copper tube such as O, S, Pb and Si can be significantly reduced, and the average columnar dendrite spacing of the copper tube can also be reduced from 2.21 mm to 0.93 mm by adding La. The ultimate tensile strength and the elongation with and without La addition are almost unchanged. However, the annual corrosion rate of the HCC TP2 copper tube is reduced from 10.18 mm·a^(-1) to 9.37 mm·a^(-1) by the purification effect of trace La.

著录项

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号