首页> 中文期刊> 《中国铸造：英文版》 >Microstructure characteristics and solidification behavior of wrought aluminum alloy 2024 rheo-diecast with self-inoculation method

Microstructure characteristics and solidification behavior of wrought aluminum alloy 2024 rheo-diecast with self-inoculation method

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

One important problem in casting wrought aluminum alloys is the high tendency to the formation of hot tears in the solidification process.By using semi-solid metal(SSM) processing,the hot tearing tendency of alloys can be minimized during casting.In the present research,the semi-solid slurry of wrought aluminum alloy 2024 was firstly prepared with a novel self-inoculation method(SIM),and then the microstructure characteristics of the semi-solid slurry and the rheo-diecastings cast with the semi-solid slurry were investigated.The results indicate that finer and more uniform globular primary α-Al particles can be obtained when the semi-solid slurry are isothermally held for a short period within the semi-solid temperature range,and the primary α-Al particles without entrapped liquid are uniformly fine,globular grains in the rheo-diecastings.The holding temperature and time affect the solid fraction,particle size,and shape factor.After the semi-solid slurry is held at 625 ℃ for 3 min and 5 min,the optimal values for the average equivalent diameter are 70.80 μm and 74.15 μm,and for the shape factor are 1.32 and 1.42,respectively.The solidification process of the rheo-diecastings is composed of the following two distinct stages:primary solidification process and secondary solidification process.The secondary solidification process consists further of the following three stages:(1) direct growth of secondary primary(α 2) phase from the surface of the primary α-Al phase particles without re-nucleation,(2) independent nucleation and growth of α 3 phase from the residual liquid,and(3) eutectic reaction at the end.

著录项

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号