首页> 中文期刊> 《中国铸造：英文版》 >Effect of vibration frequency on primary phase and properties of grey cast iron fabricated by lost foam casting

Effect of vibration frequency on primary phase and properties of grey cast iron fabricated by lost foam casting

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The properties of gray cast iron(GCI)are affected by density of matrix,size of flake graphite and primary austenite.In this paper,the Y-type specimen of GCI was prepared by lost foam casting(LFC)with and without vibration,and the influence of vibration frequency on the density of matrix,size of primary phase,and properties of the GCI was studied.The results show that the length of the flake graphite and the size of the primary austenite in GCI firstly decrease and then increase with the increase of the vibration frequency.With a vibration frequency of 35 Hz,the length of the flake graphite is the shortest,the primary austenite is the finest and the density of the matrix is the highest.In addition,the tensile strength,elongation and hardness of the GCI firstly increase and then decrease with the increase of the vibration frequency,due to the refinement of the primary phase and the increase of the matrix density.In order to analyze the refinement mechanism of the primary phase of the GCI fabricated by the LFC with vibration,the solidification temperature fields of the GCI fabricated by the LFC with the vibration frequency of 0 and 35 Hz were measured.The results show that the vibration reduces the eutectic point of the GCI and increases the supercooling degree during the eutectic transformation.As a result,the length of the flake graphite and the size of the primary austenite in GCI fabricated by LFC with the vibration frequency of 35 Hz decrease.

著录项

相似文献

  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号