首页> 中文期刊> 《中国铸造：英文版》 >Microstructure evolution and its effect on mechanical properties of cast Ti48Al6NbxSi alloys

Microstructure evolution and its effect on mechanical properties of cast Ti48Al6NbxSi alloys

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In order to improve mechanical properties of TiAlNb alloys,different contents of silicon were added into Ti48Al6Nb alloy.The Ti48Al6NbxSi (x=0,0.1,0.2,0.3,0.4 and 0.5,at.%) alloys were prepared by vacuum arc melting.The phase constitution,microstructure evolution and mechanical properties of the alloys were studied.Results show that the Ti48Al6NbxSi alloys consist of γ-TiAl phase,α2-Ti3Al phase and B2 phase,and Ti5Si3 silicide phase is formed when the addition of silicon is higher than 0.3at.%.The addition of silicon leads to the decrease in γ phase and increase in α2 phase.The formation of silicide decreases the amount of Nb dissolved in the TiAl matrix,and therefore decreases B2 phase.Compressive tests show that the ultimate strength of the alloys increases from 2,063 MPa to 2,281 MPa with an increase in silicon from 0 to 0.5at.%,while the fracture strain decreases from 34.7% to 30.8%.The increase of compressive strength and decrease of fracture strain can be attributed to the decrease of B2 phase and the formation of Ti5Si3 phase by the addition of silicon.The strengthening mechanism is changed from solid solution strengthening when the addition of silicon is less than 0.3at.% to combination of solid solution strengthening and secondary phase strengthening when the addition of silicon is higher than 0.3at.%.

著录项

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号