Microstructure and microhardness of Ti-48Al alloy prepared by rapid solidification

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

To improve the microstructure and microhardness,Ti-48Al(at.%)alloy was rapidly solidified by melt spinning under different cooling rates.The microstructure and microhardness of rapidly solidified Ti-48Al alloy were systematically investigated.Results show that the average lamellar colony size of the alloy reduces from 60.6μm to 11μm as the cooling rate increases from 2.3×105 to 5.1×105 K·s-1,caused by the increase of nucleation rate at a higher cooling rate.At the high cooling rate of(4.3-5.1)×105 K·s-1,theαphase is the primary phase,and a few metastableαphases are reserved,which then transform intoα2 phase and subsequently lead to the formation ofα2 equiaxed grain.The lamellar spacing also decreases with the increase of cooling rate.The relationship between lamellar spacing(d)and cooling rate(v)is d=33.6v-1.34.The microhardness increases with the increase of cooling rate because the refined lamellar spacing and grain size can improve the microhardness.

著录项

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号