首页> 中文期刊> 《中国铸造》 >Shear bands of as-cast and semi-solid Ti48Zr27Cu6Nb5Be14 bulk metallic glass matrix composites

Shear bands of as-cast and semi-solid Ti48Zr27Cu6Nb5Be14 bulk metallic glass matrix composites

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The as-cast Ti48Zr27Cu6Nb5Be14 bulk metallic glass matrix composites（BMGMCs） were fabricated using a copper mold suction casting method. Then, the semi-solid BMGMC samples were obtained following an isothermal treatment（heating at 900 °C for 10 min, then cooling with water）. The microstructure and compression property were investigated by scanning electronic microscopy（SEM） and universal mechanical tester. As a result of the isothermal treatment, the crystal shapes change from fine, granular, and dendritic to spherical or vermicular, and the average crystal size of the as-cast and semi-solid samples is 2.2 μm and 18.1 μm, respectively. The plasticity increases from 5.31% in the as-cast to 10.23% in the semi-solid samples, with an increase of 92.66%. The shear bands from different areas of the side surfaces of as-cast and semisolid compression fracture samples were observed. The characteristic changes of multiplicity, bend, branch and intersection of shear bands in different areas indicate that the deformation of as-cast and semi-solid samples is non-uniform during compression. It is found that poor plasticity of the as-cast samples or good plasticity of the semi-solid samples are reflected by characteristics of the shear bands. The semi-solid isothermal treatment improves the plasticity by forming large crystals which can block the expansion of shear bands and promote the multiplicity of shear bands.

著录项

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号