Influence of hot isostatic pressing on microstructure,properties and deformability of selective laser melting TC4 alloy

开具论文收录证明 >>

期刊封面封底目录下载 >>

文献代查 >>

页面导航

摘要
著录项
相似文献
相关主题

摘要

The influence of different hot isostatic pressing regimes on microstructure,phase constitution,microhardness,tensile properties and deformability of TC4 alloy fabricated by selective laser melting(SLM)technology was studied.The results show that the microstructure of SLM TC4 alloy is composed of acicular martensiteα’phase,and the sample exhibits high microhardness and strength,but low plasticity.After hot isostatic pressing,acicular martensiteα’phase transforms intoα+βphase,and with the increase of hot isostatic pressing temperature and duration,αphase with coarse lath is gradually refined,and the proportion ofαphase is gradually reduced.Because of the change of phase constitution in SLM TC4 alloy after hot isostatic pressing,the grain refinement strengthening is weakened,the density of dislocation is reduced,so that both microhardness and tensile strength are decreased by around 20%,the elongation is increased by more than about 70%,even over 100%,compared with as-deposited TC4 alloy.When the hot isostatic pressing regime is 940°C/3 h/150 MPa,the tensile strength and the elongation achieve optimal match,which are about890 MPa and around 14.0%in both directions.The fracture mechanism of alloy after 940 oC/3 h/150 MPa HIP is dultile fracture.Hot isostatic pressing causes concave deformation of SLM TC4 alloy thin-walled frames,and the deformation degree increases with the increase of temperature.

著录项

来源
《中国铸造：英文版》 |2021年第4期|389-396|共8页
作者
Tai-qi Yan; Bing-qing Chen; Xia Ji; Shao-qing Guo;
展开▼
作者单位

3D Printing Research and Engineering Technology Center;

Beijing Institute of Aeronautical Materials;

Beijing 100095;

China;

Falcon Fast Manufacturing Technology Co.;

Ltd.;

Wuxi 214145;

Jiangsu;

China;

展开▼
原文格式 PDF
正文语种 chi
中图分类 TG146.23;
关键词
selective laser melting; TC4 alloy; hot isostatic pressing; microstructure; mechanical properties; deformability;

相似文献

中文文献
外文文献
专利

1. Impact of laser scanning speed on microstructure and mechanical properties of Inconel 718 alloys by selective laser melting [J] . Hong-ying Wang ,Bin-bin Wang ,Liang Wang . 中国铸造 . 2021,第003期
2. Microstructure and properties of AlSi7Mg alloy fabricated by selective laser melting [J] . Shuai Huang ,Shao-qing Guo ,Biao Zhou . 中国铸造 . 2021,第004期
3. Effects of hot isostatic pressing temperature on casting shrinkage densification and microstructure of Ti6Al4V alloy [J] . Qian Xu ,Jian-xin Zhou ,Hai Nan . 中国铸造 . 2017,第005期
4. Laser　Surface　Melting　of　Plastics　Mold　Steels　by　Automated　Nd..YAG　Laser　System [C] . . 自动化科学技术应用学术会议 . 2001
5. Microstructure and Properties ofγ-TiAl Based Alloys Fabricated by Selective Laser Melting Technique [A] . Adam Ismaeel Ibrahim . 2018

Influence of hot isostatic pressing on microstructure,properties and deformability of selective laser melting TC4 alloy

摘要

著录项

相似文献

相关主题

期刊订阅