Three kinds of retardant systems, single-component Al （OH） 3, Al （OH） 3-Mg （OH） 2, and Al（OH）3-OMMT, were applied in cable jacket material and their effects on flame retarding performance and mechanical properties were studied. When the weight ratio of Al （OH）3 and Mg（OH）2 was 1 ： 1, these materials have good flame retardant property. A synergistic effect between Al（OH）3 and OMMT was confirmed by the formation of compact charred layer. Singlecomponent Al（OH）3 also showed a significant effect on flame retardancy.%研究了氢氧化铝-氢氧化镁[Al（OH）3-Mg（OH）2]和Al（OH）3-有机蒙脱土（OMMT）这两种不同的阻燃体系以及不同生产工艺制备的单组分Al（OH）3对电缆护套料的阻燃性能和力学性能的影响。结果表明，Al（OH）3和Mg（OH）2的添加量为1：1时，电缆护套料的阻燃性能达到比较理想的效果；加入3％的OMMT能与Al（OH）s在燃烧过程中产生良好的协同效应，生成致密且坚固的炭层，改善了电缆护套料的阻燃性能；不同生产工艺制备的Al（OH）3用作电缆护套料的阻燃剂，能明显提高其阻燃性能。