首页> 中文期刊> 《合成纤维工业》 >索式萃取法测定聚丙烯腈原丝的含油率

索式萃取法测定聚丙烯腈原丝的含油率

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

采用索氏萃取法测定聚丙烯腈(PAN)原丝的含油率,分析了萃取剂配比、萃取温度、萃取时间及萃取次数对测试结果的影响,探讨了原丝含油率与灰分含量之间的关系.结果表明:采用索氏萃取法测试PAN原丝含油率的最佳条件为萃取剂甲醇和氯仿体积比为1/1.5 ～ 1/2.5,萃取温度为80～85℃,萃取时间为2.5h,萃取次数为1;此方法的回收率为97.8％～103.1％,相对标准偏差为1.14％,但该法只能测试PAN原丝表面的油剂含量,渗透至原丝内部的油剂难以萃取出来,可通过烧蚀后的灰分含量来反映.%The oil content of polyacrylonitrile (PAN) precursor was determined by soxhlet extraction method.The effects of extractant proportion and extraction temperature,time and number on the determination results were analyzed.The relationship between oil and ash contents was discussed.The results showed that the Soxhlet extraction determination had the recovery rate of 97.8％-103.1％ and relative standard deviation of 1.14％ under the conditions of methanol and chloroform extractants at the volume ratio of 1/1.5-1/2.5,extraction temperature 80-85 ℃,extraction time 2.5 h,extraction number 1 ; and this method could be only used to determine the oil content on the surface of PAN precursor as the ashes after high-temperature burting could be a reflection of oil content in fiber interior due to the difficulties in extracting the oil out of the fiber.

著录项

  • 来源
    《合成纤维工业》 |2013年第4期|68-70,73|共4页
  • 作者

    皇静; 钱鑫; 王微霞; 钟俊俊; 王雪飞; 李德宏; 杨建行;

  • 作者单位

    中国科学院宁波材料技术与工程研究所碳纤维制备技术国家工程实验室,宁波315201;

    中国科学院宁波材料技术与工程研究所碳纤维制备技术国家工程实验室,宁波315201;

    中国科学院宁波材料技术与工程研究所碳纤维制备技术国家工程实验室,宁波315201;

    中国科学院宁波材料技术与工程研究所碳纤维制备技术国家工程实验室,宁波315201;

    中国科学院宁波材料技术与工程研究所碳纤维制备技术国家工程实验室,宁波315201;

    中国科学院宁波材料技术与工程研究所碳纤维制备技术国家工程实验室,宁波315201;

    中国科学院宁波材料技术与工程研究所碳纤维制备技术国家工程实验室,宁波315201;

  • 原文格式 PDF
  • 正文语种 chi
  • 中图分类 聚丙烯腈系纤维;产品分析与检验;
  • 关键词

    聚丙烯腈纤维; 含油率; 测定; 索式萃取法; 准确度; 精密度;