首页> 中文期刊> 《中国焊接：英文版》 >Evolution behavior of phase and performance in Ni-based coating layer based on high temperature thermal field

Evolution behavior of phase and performance in Ni-based coating layer based on high temperature thermal field

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Effect of post-welding heat treatment on the microstructure and properties of BNi-2 brazing coating was analyzed. The phase transformation in the heat treatment process was analyzed by high temperature metallographic microscope, scanning electron microscope and X-ray diffraction, and the microhardness after the post heat treatment was tested by microhardness tester. The results show that the microstructure of brazing BNi-2 brazing coating is mainly CrB phase, Ni solid solution phase and eutectic phase of Ni_(3)B and Ni_(3)Si. After brazing,the overall hardness value is higher, generally higher than 510 HV, and the microhardness in some areas is higher than 700 HV. After quenching, the solid solution phase of Ni increased, and the eutectic phase of Ni and Ni_(3)Si decreased, leading to the softening of the brazing coating, the area whose microhardness in the range of 342 HV–454 HV increased. After tempering the brazed coating samples, the eutectic phases of Ni and Ni_(3)Si grew and the hardness recovered, but the overall hardness distribution was still lower than the brazing one. The results of the brazing post-heat treatment test show that the post-welding heat treatment will bring adverse effects on the hardness distribution of the coating, which may affect the wear resistance of the coating.

著录项

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号