The hydrogenation of petroleum resin(PR)is an effective process to prepare high value-added hydrogenated PR(HPR).However,the preparation of non-noble metal-based catalysts with high catalytic activity for PR hydrogenation still remains a challenge.Herein,a La promoted Ni-based catalyst is reported through the thermal reduction of quaternary Ni La Mg Al-layered double hydroxides(Ni La Mg Al-LDHs).The incorporation of La is beneficial to the reduction and stability of Ni particles with reduced particle size,and the increased alkalinity effectively mitigates the breakage of molecular chains of PR.As a result,the La promoted Ni-based catalyst exhibits high catalytic activity and excellent stability for PR hydrogenation.A hydrogenation degree of 95.4%and 96.1%can be achieved for HC_(5)PR and HC_(9) PR with less reduced softening point,respectively.Notably,the hydrogenation degree still maintains at 92.7%even after 100 hours’reaction,much better than that without La incorporation or prepared using conventional impregnation method.