首页> 中文期刊> 《牙体牙髓牙周病学杂志》 >3D打印氧化锆全瓷冠的密合性研究

3D打印氧化锆全瓷冠的密合性研究

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

目的:评估3D打印技术与CAD/CAM切削技术制作的氧化锆全瓷单冠的密合性.方法:分别采用3D打印(实验组)和CAD/CAM切削(对照组)各制作10个氧化锆全瓷单冠,通过"硅橡胶法"和三维偏差分析软件Geomagic Qualify测量其冠边缘及内部的密合性,并对结果进行统计分析.结果:全瓷冠的边缘及内部密合性(μm)3D打印组分别为89 ± 19、87 ± 16, CAD/CAM切削组分别为94 ± 31、107 ± 33(P>0.05).结论:3D打印技术制作的氧化锆全瓷单冠的密合性能满足临床要求.%AIM: To evaluate the fitness of zirconia single crowns fabricated with 3D printing. METH-ODS:Zirconia single crowns were processed by a 3D printing system(test group,n=10) and by a CAD/CAM milling system (control group,n=10)respectovely. Marginal fit and internal fit were examined using a light-body silicone and a 3D inspection software-Geomagic Qualify.The independent sample test was used to determine statistically signif-icancy between the 2 groups by SPSS statistical package version 22.0. RESULTS:The fitness of marginal and internal of the crowns was (89 ± 19)μm and(87 ± 16)μm respectively of the 3D printing group, (94 ± 31)μm and (107 ± 33)μm respectively of the milling group(between 2 groups,P>0.05). CONCLUSION:The fitness of zirco-nia single crown produced by 3D printing meet the clinical requirements.

著录项

  • 来源
    《牙体牙髓牙周病学杂志》 |2018年第4期|209-213|共5页
  • 作者

    王伟娜; 于海; 刘一帆; 高勃;

  • 作者单位

    军事口腔医学国家重点实验室,口腔疾病国家临床医学研究中心,陕西省口腔医学重点实验室,第四军医大学口腔医院,修复科,陕西 西安710032;

    军事口腔医学国家重点实验室,口腔疾病国家临床医学研究中心,陕西省口腔医学重点实验室,第四军医大学口腔医院,修复科,陕西 西安710032;

    军事口腔医学国家重点实验室,口腔疾病国家临床医学研究中心,陕西省口腔医学重点实验室,第四军医大学口腔医院,关节病科,陕西 西安710032;

    军事口腔医学国家重点实验室,口腔疾病国家临床医学研究中心,陕西省口腔医学重点实验室,第四军医大学口腔医院,修复科,陕西 西安710032;

  • 原文格式 PDF
  • 正文语种 chi
  • 中图分类 牙体缺损的修复矫治;
  • 关键词

    3D打印; CAD/CAM切削; 全瓷冠; 密合性;

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号