The microstructures and mechanical properties of Mg-8Li and Mg-8Li-2Al-2RE alloy sheets were evaluated after cold rolling.Both alloys contain α-phase and β-phase which consists of a solid solution of Mg in BCC Li.The proportion ofβ-phase in both alloys is approximately 60%.Theα-phase andβ-phase are elongated approximately parallel to the rolling direction and there is no sign of recrystallization even after being annealed at 200℃for 1 h.The yield strength of Mg-8Li-2Al-2RE sheets is about 165 MPa with elongation of 35%along rolling direction,while the yield strength is about 187 MPa with elongation of 21%along the direction titled 45ü to rolling direction.Theα-phase in both alloys exhibits basal texture,and the intensity of basal texture in Mg-8Li is larger than that in Mg-8Li-2Al-2RE.However,theβ-phase shows（100）texture,and the intensity of（100）texture in Mg-8Li is twice of that in Mg-8Li-2Al-2RE.It could be attributed to the existence of RE-containing particles in Mg-8Li-2Al-2RE.