Oxygen ion conductivity of La_(0.8)Sr_(0.2)Ga_(0.83)Mg_(0.17-x)Co_xO_(3-δ) synthesized by laser rapid solidification

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Materials La0.8Sr0.2Ga0.83Mg0.17-xCoxO3-δ with x = 0, 0.05, 0.085, 0.10, and 0.15 are synthesized by laser rapid solidification. It is shown that the samples prepared by laser rapid solidification give rise to unique spear-like or leaf-like microstructures which are orderly arranged and densely packed. Their electrical properties each show a general dependence of the Co content and the total conductivities of La 0.8 Sr 0.2 Ga 0.83 Mg 0.085 Co 0.085 O 3-δ prepared by laser rapid solidification are measured to be 0.067, 0.124, and 0.202 S·cm -1 at 600, 700, and 800℃, respectively, which are much higher than by conventional solid state reactions. Moreover, the electrical conductivities each as a function of the oxygen partial pressure are also measured. It is shown that the samples with the Co content values ≤ 8.5 mol% each exhibit basically ionic conduction while those for Co content values ≥ 10 mol % each show ionic mixed electronic conduction under oxygen partial pressures from 10 -16 atm (1 atm = 1.01325×10 5 Pa) to 0.98 atm. The improved ionic conductivity of La 0.8 Sr 0.2 Ga 0.83 Mg 0.085 Co 0.085 O 3-δ prepared by laser rapid solidification compared with by solid state reactions is attributed to the unique microstructure of the sample generated during laser rapid solidification.

著录项

相似文献

  • 中文文献
  • 外文文献
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号