首页> 中文期刊> 《中国物理：英文版》 >Thermal stability and electrical properties of copper nitride with In or Ti

Thermal stability and electrical properties of copper nitride with In or Ti

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Thin films of ternary compounds CuxInyN and CuxTiyN were grown by magnetron sputtering to improve the thermal stability of Cu3N,a material that decomposes below 300℃,and thus promises many interesting applications in directwriting.The effect of In or Ti incorporation in altering the structure and physical properties of copper nitride was evaluated by characterizing the film structure,surface morphology,and temperature dependence of electrical resistivity.More Ti than In can be accommodated by copper nitride without completely deteriorating the Cu3N lattice.A small amount of In or Ti can improve the crystallinity,and consequently the surface morphology.While the decomposition temperature is rarely influenced by In,the Ti-doped sample,Cu59.31Ti2.64N38.05,shows an X-ray diffraction pattern dominated by characteristic Cu3N peaks,even after annealing at 500℃.Both In and Ti reduce the bandgap of the original Cu3N phase,resulting in a smaller electrical resistivity at room temperature.The samples with more Ti content manifest metal-semiconductor transition when cooled from room temperature down to 50 K.These results can be useful in improving the applicability of copper-nitride-based thin films.

著录项

相似文献

  • 中文文献
  • 外文文献
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号