A new method for preparation of TaC coating on C/C composite material is reported. The amorphous ethylate tantalum jellied as the precursor is prepared and spread densely on the surface of the C/C composite material so as to form a multilayer film. In a graphitization furnace the multilayer film is transformed into TaC coating at various temperatures. Ethylate tantalum film is characterized by FT-IR (Fourier transform infrared) spectra, XRD (X-ray diffraction) and SEM (scanning electron microscopy) and TaC coating is characterized by XRD and SEM. At 1200℃the coating contained TaC and Ta2O5, and at above 1400℃ only TaC is formed. The coating formed at 1600℃ is a continuous stratum structure, and that formed at 1600℃ is a porous net structure. Analysis on thermodynamics and formation mechanism of TaC indicates that, after ethylate tantalum is decomposed, Ta2O5 is first produced and then transformed into Ta2C, and newly formed Ta2C is transformed into TaC by the sufficient C at last.
展开▼
机译：How the Group Leaders of Lesson Preparation Groups Facilitate Group Learning and Reflective Practice in Chinese Public High Schools =中国公立高中的备课组长是如何引领团队学习和反思性实践的？
机译：连续纤维增强复合材料的湿热效应。第一部分。复合材料中的热和水分扩散（Effets Hygrothermiques dans les Composites a Renfort de Fiber Continu.partie I. Diffusion de L'Humidite et de la Chaleur dans les materiaux Composites。