首页> 中文期刊> 《工程塑料应用》 >ABS微孔发泡材料的制备与性能研究

ABS微孔发泡材料的制备与性能研究

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Microcellular acrylonitrile-butadiene-styrene ( ABS ) foam was prepared by chemical cross-linked compression molding. The effects of foaming agent ( AC), activator (ZnO ), crosslink agent ( DCP ) on the mechanical properties and cell structure of microcellular ABS foam were researched. The results showed that when the content of foaming agent, crosslink agent and activator were 2%, 0.15%, 0.2%, the cell density was 1.31 x 10s cells/cm3, the cell dimension was 24 μm and the specific strength was up to 44.7 N/tex. The microcellular ABS foam had excellent properties, which met the requirements of microcellular foam material.%利用化学交联模压法制备了丙烯腈-丁二烯-苯乙烯塑料(ABS)微孔发泡材料,研究了发泡剂偶氮二甲酰胺(AC)、活化剂氧化锌( ZnO)、交联剂过氧化二异丙苯(DCP)用量对ABS微孔发泡材料力学性能和泡孔结构形态的影响.结果表明,当AC为2份、DCP为0.15份、ZnO为0.2份时,制得的ABS微孔发泡材料的泡孔密度为1.31×108 cells/cm3,平均泡孔尺寸为24 μm,比强度达到44.7 N/tex,综合性能最佳,可以满足微孔发泡材料的要求.

著录项

  • 来源
    《工程塑料应用》 |2012年第1期|12-15|共4页
  • 作者

    虞吉钧; 杨永兵; 岳邦毅; 罗国菁; 李锦春; 陈强;

  • 作者单位

    常州大学材料科学与工程学院,江苏常州 213164;

    南京大学常州高新技术研究院,江苏常州 213164;

    南京大学常州高新技术研究院,江苏常州 213164;

    南京大学常州高新技术研究院,江苏常州 213164;

    常州大学材料科学与工程学院,江苏常州 213164;

    南京大学常州高新技术研究院,江苏常州 213164;

    常州大学材料科学与工程学院,江苏常州 213164;

    常州大学材料科学与工程学院,江苏常州 213164;

    南京大学常州高新技术研究院,江苏常州 213164;

    南京大学化学化工学院,南京 210093;

  • 原文格式 PDF
  • 正文语种 chi
  • 中图分类 泡沫塑料;
  • 关键词

    丙烯腈-丁二烯-苯乙烯塑料; 微孔发泡; 模压法; 化学交联;

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号