摘要

目的 研究几种典型金属材料在西沙海洋飞溅区的腐蚀行为规律.方法 通过外场暴露试验,分析3种钢、1种铜和3种铝合金材料暴露0.5,1,2 a后的腐蚀形貌与动力学规律.结果 3种钢的腐蚀质量损失与点蚀均较为严重,T2整个表面均匀减薄的同时,会产生大量微小的腐蚀坑,3种铝合金发生以点蚀为主的局部腐蚀,伴随有晶间腐蚀、选择性腐蚀等.结论 试验条件下,3种钢中Q235耐蚀性最差,T2整体耐蚀性较好,3种铝合金中5083耐点蚀性能最差,5052略优于6063.%Objective To investigate the corrosion behavior and rules of typical metal materials in Xisha marine splash zone.Methods Field exposure test was carried out on 3 kinds of steels, 1 kind of copper and 3 kinds of aluminium alloy materials for 0.5 a, 1 a and 2 a to analyze their corrosion morphology and kinetics rule.Results The corrosion weight loss and pitting phenomenon for 3 kinds of steels were severe; tiny corrosion pits were formed on entire surface of T2 during its evenly thinning process; localized corrosion which was mainly composed of pits occurred on three kinds of aluminium alloy, accompanied by intergranular corrosion, selective corrosion, et al.Conclusion Under the test conditions, the corro-sion resistance of Q235 is the worst among 3 kinds of steels; T2 has a good overall corrosion resistance; pitting resistance of 5083 is the worst, while 5052 is slightly better than 6063.

著录项

  • 来源
    《装备环境工程》 |2017年第2期|51-57|共7页
  • 作者

    丁康康; 郭为民; 张彭辉; 范林; 逄昆; 孙明先;

  • 作者单位

    中国船舶重工集团公司第七二五研究所 海洋腐蚀与防护重点实验室,山东 青岛 266101;

    中国船舶重工集团公司第七二五研究所 海洋腐蚀与防护重点实验室,山东 青岛 266101;

    中国船舶重工集团公司第七二五研究所 海洋腐蚀与防护重点实验室,山东 青岛 266101;

    中国船舶重工集团公司第七二五研究所 海洋腐蚀与防护重点实验室,山东 青岛 266101;

    中国船舶重工集团公司第七二五研究所 海洋腐蚀与防护重点实验室,山东 青岛 266101;

    中国船舶重工集团公司第七二五研究所 海洋腐蚀与防护重点实验室,山东 青岛 266101;

  • 原文格式 PDF
  • 正文语种 chi
  • 中图分类 土壤腐蚀;
  • 关键词

    西沙; 飞溅区; 腐蚀; 暴露试验;

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号