ZE10 magnesium alloy was subjected to equal-channel angular pressing(ECAP) up to 12 passes in a die with an angle of 120° between the two channels at 250-300°C.An inhomogeneous microstructure of bimodal grains including fine grains of 1-2 μm as well as coarse grains of about 20 μm was obtained after the initial 1-4 ECAP passes.The grain size became increasingly homogeneous with further ECAP processing and the grains were significantly refined to 1-2 μm after 8 passes and further refined to 0.5-1 μm after 12 passes.The alloy's yield strength changed slightly but the ductility improved greatly initially up to 4-6 passes corresponding to the bimodal grain microstructure.And after the subsequent pressing of more than 8 passes,the tensile strength including yield strength improved while the elongation decreased gradually.
展开▼
机译：Microstructural evolution and mechanical properties of FeCoCrNiCu high entropy alloys:a microstructure-based constitutive model and a molecular dynamics simulation study
机译：Etude du Comportement micro-mecanique d'Une Vitroceramique a subst de siO2-al2O3-Li2O en Liaison avec la microstructure（siO2-al2O3-Li2O玻璃陶瓷的微观力学行为及其与微结构的关系研究）