[目的]研究不同工艺参数对花盆复合材料力学性能的影响.[方法]以拉伸强度、冲击强度为主要指标,采用正交及单因素试验对成型工艺进行优化.[结果]最优成型工艺务件为:热压温度185℃、热压压力12 MPa、热压时间9 min;该务件下的花盆复合材料的拉伸强度为68.76 MPa,冲击强度为9.13 KJ/m.[结论]为废弃纺织纤维复合材料的扩大应用提供了依据.%[Objective] The aim was to study the influence of different process parameters on the mechanical properties of flowerpot composite materials. [ Method] Through taking tensile strength and impact strength as the main indexes, orthogonal experiment and single factor experiment were used to optimize the molding process. [Results] The optimal molding process conditions were as follows: hot pressing temperature was 185℃, hot pressing pressure was 12 Mpa and hot pressing time was 9 min;under these conditions, tensile strength was 68.76 Mpa and impact strength was 9. 13 KJ/m. [ Conclusion] This research provided references for the expanding application of waste fiber composite materials.