首页> 中文期刊> 《哈尔滨工业大学学报：英文版》 >Effect of Surface Nanocrystallization Induced by Fast Multiple Rotation Rolling on Cr-Rare Earth-Boronizing for Steel 45 under Low-Temperature

Effect of Surface Nanocrystallization Induced by Fast Multiple Rotation Rolling on Cr-Rare Earth-Boronizing for Steel 45 under Low-Temperature

         
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

In this paper,fast multiple rotation rolling( FMRR) is applied to fabricate a nanostructured layer on the surface of steel 45. The FMRR samples are then Cr-Rare earth-boronized under low-temperature. The boride layer is characterized by using Scanning electron microscopy( SEM) and X-ray diffraction( XRD).Experimental results indicate that the thickness of the boride layer is greatly increased by surface nanocrystallization. The boride layer with relatively continuous structure instead of the zigzag teeth structure is obtained,and the penetrating rate is enhanced by 2. 5-3. 7 times when the FMRR samples are Cr-Rare earthboronized at the temperature of 570 ℃,600 ℃ and 650 ℃ for 6 h. The boride layer fabricated on the FMRR sample consists of single phase Fe2 B. Severe plastic deformation with the grain size of approximately 100 nm in the top surface layer of steel 45 is observed,and the thickness of the plastic deformation layer is about 30 μm.The microstructure in the top surface layer is characterized by Transmission electron microscopy( TEM). Grain boundaries are largely increased with high stacking fault energy after FMRR, leading to a significant enhancement of RE boron-chromizing speed.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号