Effect of Sulfur Content and Sulfide Shape on Fracture Ductility in Case Hardening Steel

XIAO Guo-hua; DONG Han; WANG Mao-qiu; HUI Wei-jun

首页> 中文期刊> 《钢铁研究学报（英文版）》 >Effect of Sulfur Content and Sulfide Shape on Fracture Ductility in Case Hardening Steel

Effect of Sulfur Content and Sulfide Shape on Fracture Ductility in Case Hardening Steel

开具论文收录证明 >>

文献代查 >>

页面导航

摘要
著录项
相关主题

摘要

The effects of sulfur content and calcium addition on smooth axisymmetric tensile fracture ductility of case hardening steel DIN 18CrNiMo7-6 have been investigated. The quantitative metallographic analysis of sulfide inclusions and the correlations between sulfide inclusions and fracture ductility were examined. Sulfide inclusions were found to have deleterious effect on fracture ductility, whereas the effect can be offset to some extent by calcium-treat- ment due to less easily deforming of sulfides during hot-working. The product （AA·λAW） of sulfide inclusion area fraction （An） and its area-weighted aspect ratio （λAW） can be used as a parameter to describe the effect of sulfide inclusions on fracture true strain.

著录项

来源
《钢铁研究学报（英文版）》 |2011年第8期|58-64|共7页
作者
XIAO Guo-hua; DONG Han; WANG Mao-qiu; HUI Wei-jun;
展开▼
作者单位

National Engineering Research Center of Advanced Steel Technology, Central Iron andSteel Research Institute, Beijing 100081, China;

National Engineering Research Center of Advanced Steel Technology, Central Iron andSteel Research Institute, Beijing 100081, China;

National Engineering Research Center of Advanced Steel Technology, Central Iron andSteel Research Institute, Beijing 100081, China;

National Engineering Research Center of Advanced Steel Technology, Central Iron andSteel Research Institute, Beijing 100081, China;

展开▼
原文格式 PDF
正文语种 chi
中图分类钢包精炼炉;
关键词
硫化物夹杂; 表面硬化钢; 拉伸断裂; 硫含量; 形状; 延性; 定量金相; 断裂韧性;

机译：硫化物夹杂;表面硬化钢;拉伸断裂;硫含量;形状;延性;定量金相;断裂韧性;

Effect of Sulfur Content and Sulfide Shape on Fracture Ductility in Case Hardening Steel