>Effect of annealing time on the exchange coupling interactions and microstruc-ture of nanocomposite Pr_(7.5)Dy_1Fe_(71)Co_(15)Nb_1B_(4.5) ribbons
Effect of annealing time on the exchange coupling interactions and microstruc-ture of nanocomposite Pr_(7.5)Dy_1Fe_(71)Co_(15)Nb_1B_(4.5) ribbons
The influence of annealing time on the magnetic properties and microstructure of nanocomposite Pr7.5Dy1Fe71Co15Nb1B4.5 ribbons was systematically investigated by the methods of vibrating sample magnetometer (VSM), X-ray diffraction (XRD) and high resolution transmission electron microscopy (HRTEM). Interaction domains derived from strong exchange coupling interactions be- tween hard and soft magnetic grains were imaged using magnetic force microscopy (MFM). Maximum remanence, intrinsic coerciv- ity, and maximum energy product values were obtained in the ribbons annealed at 700°C for 15 min, which were composed of Pr2(Fe, Co)14B, α-(Fe, Co), and slight Pr2(Fe, Co)17 phases. Although Jr, Hci, and (BH)max decreased gradually with further increase of an- nealing time, it is emphasized that comparatively high Jr and Hci and (BH)max were obtained in a wide annealing time period of 15 to 360 min. The shape of initial magnetization curves and hysteresis loops change as a function of annealing time, indicating different magnetization reversal routes, which can be fully explained by the corresponding microstructure.
展开▼