Four types of steel sheets containing 0.04%,0.09%,0.14%and 0.36%Si,respectively,were electrodeposited with a nickel layer of 3μm in thickness and then galvanized in molten Zn at 450℃for various periods of time.The formation and growth of intermetallic compound layers on the surface of the samples were investigated by SEM and EDS.The experimental results show that the method of Ni-electrodeposited pretreatment can distinctively restrain the over-growth of the galvanized coatings of reactive steels and get eligible coatings with a proper thickness,bright appearance and strong adherence.EDS results indicate that a series of Ni-Zn intermetallic compoundsγ',γandδ 2 are first formed on the surface of the samples.With a prolonged immersion time,theΓ 2 -Fe-Zn-Ni andδ-Fe-Zn are formed accompanied by the gradual disappearance ofγ′,γandδ 2 layer.After a longer immersion time,the lumpyζ-Fe-Zn occurs betweenδand liquid Zn and the Г-Fe-Zn does between steel substrate andδ.Subsequently,ζis in the form of a continuous and compact layer. The method of Ni-electrodeposited pretreatment changes the formation of Fe-Zn intermetallic compounds,which delay the growth of lumpyζand promote the growth of compactδ.Consequently,the abnormal growth of reactive steels is eliminated.
展开▼