首页> 中文期刊> 《中国材料进展》 >激光焊接Ti-6Al-4V钛合金塑性行为的原位SEM/EBSD分析

激光焊接Ti-6Al-4V钛合金塑性行为的原位SEM/EBSD分析

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

EBSD and in-situ SEM were used to study the plastic behavior of laser beam welding Ti-6Al-4V.Due to the high weld temperature(exceeding the β-transus) and high cooling rate,β→α' martensitic transformation occurs.Within the fusion zone,only acicular morphology exists,while in 1st heat affected zone(HAZ) and 2ndHAZ,these acicular laths globalize,which show an obvious microstructural gradient.The result of the in-situ plastic deformation shows the deformation can be divided into 2 stages.In the first stage of the deformation,either slipping or twinning can occur.It depends on whether the initial orientation can respect //TA(tensile axis) by rotating the grains or not.While in the second stage,only slipping can be found.%选用原位SEM/EBSD显微术分析研究了Ti-6Al-4V钛合金的焊接区域的变形行为.研究发现,由于焊接时高的焊接温度(在β相变点之上)和急剧的冷却速率,导致β→α'马氏体相变的发生.SEM观察发现,在焊缝区只存在有针状的α'马氏体形貌,而在焊接第一热影响区和第二热影响区,针状α'相逐渐发生球化,形成了明显的显微组织梯度过渡.在对焊接区域进行SEM/EBSD下的原位拉伸实验后发现,该区域的塑性变形可划分为两个阶段.变形的第一阶段,滑移变形或孪生变形均有可能发生,这取决于晶粒的初始晶体学取向是否可通过旋转来匹配//TA(拉伸方向);而在变形的第二阶段,只发生滑移变形.

著录项

  • 来源
    《中国材料进展》 |2019年第3期|279-285|共7页
  • 作者

    党宁; 刘玲玉; LAVOGIEZ Cyril; MAIRE Eric; 马朝利; 周廉;

  • 作者单位

    北京航空航天大学材料科学与工程学院;

    北京100191;

    INSA de Lyon;

    Mateis UMR 5510;

    Villeurbanne 69621;

    France;

    宝钛集团有限公司;

    陕西宝鸡721014;

    INSA de Lyon;

    Mateis UMR 5510;

    Villeurbanne 69621;

    France;

    INSA de Lyon;

    Mateis UMR 5510;

    Villeurbanne 69621;

    France;

    北京航空航天大学材料科学与工程学院;

    北京100191;

    北京航空航天大学材料科学与工程学院;

    北京100191;

    西北有色金属研究院;

    陕西西安710016;

  • 原文格式 PDF
  • 正文语种 chi
  • 中图分类 TG146.23;
  • 关键词

    晶体学取向; 原位SEM; 塑性变形; 激光焊接; Ti-6Al-4V钛合金;

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号