首页> 中文期刊> 《材料导报》 >La1-xNdxB6单晶的制备及热电子发射性能

La1-xNdxB6单晶的制备及热电子发射性能

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

以LaB6和NdB6粉末为原料,采用区域熔炼法成功制备了大尺寸、高质量的多元稀土六硼化物La1-xNdxB6(x=0.1～0.3)单晶,并测试了该系列单晶(100)晶面的热电子发射性能.本实验制备的单晶长度大于40mm,直径大于4 mm.单晶衍射、劳埃照片、晶面摇摆曲线、单晶断口扫描等检测结果表明单晶质量较高,热发射测试结果表明在1 873 K、4 000V下,单晶零场电流发射密度随着Nd含量增加从6.01 A/cm2降为4.83 A/cm2,有效逸出功从2.88 eV增大到2.95 eV.%The large size high quality La1-x NdxB6 (x=0.1-0.3) single crystals had been successfully prepared by floating zone melting method using powder of LaB6 and NdB6 as raw materials.We investigated the thermionic emission performance of (100) plane of single crystals.The single crystals length was more than 40 mm and the diameter was greater than 4 mm.The single crystal tests of diffraction photographs,Laue pattern,rocking curves and fracture SEM images showed that the single crystals' quality was very high.The thermionic emission results showed that with the increase of Nd content,the null field thermionic emission current density decreased from 6.01 A/cm2 to 4.83 A/cm2 at 1 873 K,4 000 V and the average of effective work function increased from 2.88 eV to 2.95 eV.

著录项

  • 来源
    《材料导报》 |2017年第18期|21-24|共4页
  • 作者

    李录录; 张忻; 刘洪亮; 张繁星; 肖怡新; 张久兴;

  • 作者单位

    北京工业大学材料科学与工程学院,新型功能材料教育部重点实验室,北京100124;

    北京工业大学材料科学与工程学院,新型功能材料教育部重点实验室,北京100124;

    北京工业大学材料科学与工程学院,新型功能材料教育部重点实验室,北京100124;

    北京工业大学材料科学与工程学院,新型功能材料教育部重点实验室,北京100124;

    北京工业大学材料科学与工程学院,新型功能材料教育部重点实验室,北京100124;

    北京工业大学材料科学与工程学院,新型功能材料教育部重点实验室,北京100124;

    合肥工业大学材料科学与工程学院,合肥230009;

  • 原文格式 PDF
  • 正文语种 chi
  • 中图分类 陶瓷工业;
  • 关键词

    La1-xNdxB6单晶; 热电子发射; 区域熔炼; 稀土六硼化物;

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号